Hardness Testing of Plastics – Shore Durometer
HARDNESS TESTING OF PLASTICS – SHORE DUROMETER
The hardness of plastics is most commonly measured by the Shore® (Durometer) test or Rockwell Hardness Test. Both methods measure the resistance of plastics toward indentation and provide an empirical hardness value that doesn't necessarily correlate well to other properties or fundamental characteristics. Shore Hardness, using either the Shore A or Shore D scale, is the preferred method for rubbers/elastomers and is also commonly used for 'softer' plastics such as polyolefins, fluoropolymers, and vinyls. The Shore A scale is used for 'softer' rubbers while the Shore D scale is used for 'harder' ones. Many other Shore hardness scales, such as Shore O and Shore H hardness, exist but are only rarely encountered by most plastics engineers.
The Shore hardness is measured with an apparatus known as a Durometer and consequently is also known as 'Durometer hardness'. The hardness value is determined by the penetration of the Durometer indenter foot into the sample. Because of the resilience of rubbers and plastics, the indentation reading my change over time – so the indentation time is sometimes reported along with the hardness number. The ASTM test method designation is ASTM D2240 00 and is generally used in North America. Related methods include ISO 7619 and ISO 868; DIN 53505; and JIS K 6301, which was discontinued and superceded by JIS K 6253.
As seen in the charts below, the correlation between the two Shore Durometer hardness scales is weak; attempts at conversion between the scales are therefore discouraged. The correlation is higher for materials with similar resiliency properties, but is still too low for reliable conversions. Likewise, conversion between Shore Hardness and Rockwell hardness is discouraged.
Comparison of Shore Hardness Scales